由多晶氧化铝纤维经殊工艺整理切割、压缩而成。不含任何结合剂或其它成分，具有好的弹性和柔韧性,使用温度可达1600℃。在氧化气氛、中性气氛长期使用时，仍能保持其原有的韧性、强度、柔软度和纤维结构，不含渣球，可用由各种高温工业窑炉的热面内衬粘贴,隔热性能良好。
　　
　　Polycrystalline Alumina Fiber Module-cuted is from polycrystalline alumina fiber by special process finishing cutting, compression formed. Does not contain any binders or other ingredients, with excellent elasticity and flexibility, the maximum temperature up to 1600 ℃. They oxidizing atmosphere, the neutral atmosphere, the long-term bear this temperature, still maintain their original toughness, strength, flexibility and fiber structure, and non-residue ball, can be used by a variety of high-temperature industrial furnaces hot face lining paste, has a special significant insulation performance .
　　
　　产品性能
　　

　　Product specification

产品号 Product brand	化学成分, %  Chemical compositions			加热线收缩率 (24h), % Linear shrinkage on heating	导热系数w·(m·k)-1 Thermal conductivity	体积密度kg·m-3 Volume weight
	Al2O3	SiO2	Al2O3 SiO2
1600	71～73	29～27	≥99.5	＜2 （1500℃）	≤0.14（1200℃）	65-200
应  用Application	加热炉，均热炉，热处理窑，陶瓷快速烧成窑等的工作衬贴面及炉门炉盖封闭材料。 Used as module-cuted of working lining for various furnace such as heating furnace,  soaking furnace, heat treatment furnace, and ceramic fast firing kiln,  and sealing materials for furnace door or cover.
产品规格,mm Product specification	□ 标准规格： 200×100×30-80（Length * width * thickness ）    Standard: 200×100×30-80 (Length * width * thickness) □ 也可根据用户要求定做     In accordance with design drawing of user

　

　　应 用Application
　　
　　加热炉，均热炉，热处理窑，陶瓷快速烧成窑等的工作衬贴面及炉门炉盖封闭材料。
　　
　　Used as module-cuted of working lining for various furnace such as heating furnace, soaking furnace, heat treatment furnace, and ceramic fast firing kiln, and sealing materials for furnace door or cover.
　　
　　产品规格,mm
　　
　　Product specification
　　
　　标准规格： 200×100×30-80（长* 宽 *高 ）
　　
　　Standard: 200×100×30-80 (Length * width * thickness)
　　
　　也可根据用户要求定做
　　

　　In accordance with design drawing of use

　　随着高温耐火纤维产业景气度的不断提升，市场上开始有一些无生产能力，无质量保证，无售后服务的“三无”厂家或公司，借着部分热处理用户对高温陶瓷耐火纤维知识的了解不是很全面，借着部分热处理用户对高温陶瓷耐火纤维应用的风险性、安全性意识较低，通过网络宣传等手段，以价低等方式诱导热处理用户，把耐低温度级的产品充作耐高温度级，把低劣质量的多晶莫来石纤维贴面块充作高质量的，出售给热处理用户。高温纤维(多晶莫来石(氧化铝)纤维)的生产工艺控制要求比较高，其中制胶：凝胶、溶胶，成纤：热空气温度、料压、转数，干燥，中温热处理，高温热处理温度及时间等工艺数据必须精度控制，不然使用后会出现纤维内衬严重收缩、粉化、裂缝、脱落、导致窜火，不仅损坏了工业炉的仪器设备，还造成了工业炉安全生产问题，给热处理用户带来了不小的损失。